realloy classic
lei5,500.00
VAT Included
An universal CoCr bonding alloy compatible with all conventional ceramic materials
- The classic
- Excellent bonding with ceramics
- Can be melted using all known methods
- Easy finishing and easy to polish after casting
- Also suitable for laser welding
- Easy oxide removal after the ceramic firing
- Does not create dust when milling
- Worldwide proven quality
- Biocompatible
Casting Ingot
Composition
Co 63.6 % | Cr 24.8% | W 5.5 % | Mo 5.0 % | And 1.1% | Fe, Mn, Nb < 1%
This alloy is Nickel and Beryllium free and complies with EN ISO 22674, Type 4
Properties
Density 8.2 g/cm³
Vickers hardness 320 (HV10)
Linear CTE (25 - 500 °C) 14.3 (10-6·K-1)
Linear CTE (25 - 600 °C) 14.5 (10-6·K-1)
Melting range 1360 - 1420 (°C)
Casting temperature 1500 (°C)
Recommended burning temperature 980 (°C)
Proof strength (Rp 0.2) 460 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 12 (%)
Tensile strength (Rm) 675 (MPa)
Softblank
Composition
Co 63.6 % | Cr 24.8% | W 5.5 % | Mo 5.0 % | And 1.1% | Fe, Mn, Nb < 1%
This alloy is Nickel, Beryllium and lead free and complies with EN ISO 22674, Typ 4
Properties
Density 8.2 g/cm³
Vickers hardness 320 (HV10)
Linear CTE (25 - 500 °C) 14.3 (10-6·K-1)
Linear CTE (25 - 600 °C) 14.5 (10-6·K-1)
Melting range 1360 - 1420 (°C)
Recommended burning temperature 980 (°C)
Proof strength (Rp 0.2) 460 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 12 (%)
Available with or without steps
Height 10 | 12 | 14 | 16 | 18| 20 | 22 | 24 mm
Diameter Ø 98.5 mm
According to your request, it can be manufactured in different heights and diameters
Powder
Composition
Co 63.6 % | Cr 24.8% | W 5.5 % | Mo 5.0 % | And 1.1% | Fe, Mn, Nb < 1%
This alloy is Nickel and Beryllium free and complies with EN ISO 22674, Typ 5
Properties
Density 8.2 g/cm³
Vickers hardness 320 (HV10)
Linear CTE (25 - 500 °C) 14.3 (10-6·K-1)
Linear CTE (25 - 600 °C) 14.5 (10-6·K-1)
Melting range 1360 - 1420 (°C)
Casting temperature 1500 (°C)
Recommended burning temperature 980 (°C)
Proof strength (Rp 0.2) 460 (MPa)
Modulus of elasticity 200 (GPa)
Tensile elongation (A5) 12 (%)
Tensile strength (Rm) 675 (MPa)
Available particle sizes 15/45µ or 10/30µ
5kg Original special plastic box