realloy C

Price

RON 850.00

VAT Included

An universal CoCr bonding alloy compatible with all conventional ceramic materials

  • With a special composition

  • Excellent bonding with ceramics

  • Can be melted with all casting methods

  • Easy finishing and easy to polish after casting

  • Also suitable for laser welding

  • Easy oxide removal after the ceramic firing

  • Does not create dust when milling

  • Worldwide proven quality

  • Best in its class

  • Biocompatible

Tip

Casting Ingot

Composition Co 62,5 % | Cr 24,6 % | W 8,5 % | Mo 2,9 % | Si 1,3 % | Nb, Mn, Fe, N < 1,0 % This alloy is Nickel and Beryllium free and complies EN ISO 22674, Typ 4 Properties Density 8,3 g/cm³ Vickers hardness 285 (HV10) Linear CTE (25 - 500 °C) 13,9 (10-6·K-1) Linear CTE (25 - 600 °C) 14,0 (10-6·K-1) Melting interval 1304 - 1369 (°C) Casting temperature 1470 (°C) Recommended burning temperatur 980 (°C) Proof strength (Rp 0,2) 490 (MPa) Modulus of elasticity 210 (GPa) Tensile elongation (A5) 10 (%) Tensile strength (Rm) 920 (MPa)

CAD/CAM

Composition Co 62.5 % | Cr 24.6% | W 8.5 % | Mo 2.9 % | And 1.3% | Nb, Mn, Fe, N < 1.0% This alloy is Nickel and Beryllium free and complies with EN ISO 22674, Type 4 Properties Density 8.3 g/cm³ Vickers hardness 285 (HV10) Linear CTE (25 - 500 °C) 13.9 (10-6·K-1) Linear CTE (25 - 600 °C) 14.0 (10-6·K-1) Melting range 1304 - 1369 (°C) Casting temperature 1470 (°C) Recommended burning temperature 980 (°C) Proof strength (Rp 0.2) 490 (MPa) Modulus of elasticity 210 (GPa) Tensile elongation (A5) 10 (%) Tensile strength (Rm) 920 (MPa)  

Available with or without steps

Height  8| 10 | 12 | 13.5 | 14 | 15 | 16 | 18| 20 | 22 | 24 mm

Diameter Ø 98.5 mm or without ste 99.5 mm

According to your request, it can be manufactured in different heights and diameters

Softblank

Composition Co 62,5 % | Cr 24,6 % | W 8,5 % | Mo 2,9 % | Si 1,3 % | Nb, Mn, Fe, N < 1,0 % This alloy is Nickel and Beryllium free and complies EN ISO 22674, Typ 4 Properties Density 8,3 g/cm³ Vickers hardness 285 (HV10) Linear CTE (25 - 500 °C) 13,9 (10-6·K-1) Linear CTE (25 - 600 °C) 14,0 (10-6·K-1) Melting interval 1304 - 1369 (°C) Casting temperature 1470 (°C) Recommended burning temperatur 980 (°C) Proof strength (Rp 0,2) 490 (MPa) Modulus of elasticity 210 (GPa) Tensile elongation (A5) 10 (%)  

Available with or without step

Height  10 | 12 | 14 | 16 | 18 | 20 | 22 | 24 mm

Diameter Ø 98,5 mm  

According your request, can be manufactured in different heights and diameters

Powder

Composition Co 62,5 % | Cr 24,6 % | W 8,5 % | Mo 2,9 % | Si 1,3 % | Nb, Mn, Fe, N < 1,0 % This alloy is Nickel and Beryllium free and complies EN ISO 22674, Typ 5 Properties Partical sizes 15/45µ or 10/30µ Density 8,3 g/cm³ Vickers hardness 515 (HV10) Linear CTE (25 - 500 °C) 13,9 (10-6·K-1) Linear CTE (25 - 600 °C) 14,0 (10-6·K-1) Melting interval 1304 - 1369 (°C) Recommended burning temperatur 980 (°C) Proof strength (Rp 0,2) 1047 (MPa) Modulus of elasticity 171 (GPa) Tensile elongation (A5) 2,4 (%) Available partical sizes 15/45µ or 10/30µ 5kg Original special plastic box